典型拉伸性能
Stress relieved
|
Stress Relieved Temperature
|
Stress Relieved Testing Time
|
保護(hù)氣體
|
屈服強度
|
延伸率
|
抗拉強度
|
760 °C
|
2 hr
|
Ar (I1) EN
|
690 MPa
|
20 %
|
785 MPa
|
760 °C
|
2 hr
|
Ar (I1) EN
|
420 MPa
|
22 %
|
450 MPa
|
760 °C
|
2 hr
|
Ar (I1) EN
|
500 MPa
|
16 %
|
560 MPa
|
760 °C
|
2 hr
|
Ar (I1) EN
|
510 MPa
|
14 %
|
580 MPa
|
735 °C
|
4 hr
|
Ar (I1) EN
|
670 MPa
|
20 %
|
760 MPa
|
夏比V型缺口沖擊性能
Stress relieved
|
Stress Relieved Testing Temp
|
Stress Relieved Testing Time
|
保護(hù)氣體
|
沖擊值
|
測試溫度
|
760 °C
|
2 hr
|
Ar (I1) EN
|
200 J
|
20 °C
|
760 °C
|
2 hr
|
Ar (I1) EN
|
180 J
|
0 °C
|
760 °C
|
2 hr
|
Ar (I1) EN
|
150 J
|
-20 °C
|
760 °C
|
2 hr
|
Ar (I1) EN
|
90 J
|
-40 °C
|
760 °C
|
2 hr
|
Ar (I1) EN
|
70 J
|
-60 °C
|
735 °C
|
4 hr
|
Ar (I1) EN
|
210 J
|
20 °C
|
735 °C
|
4 hr
|
Ar (I1) EN
|
190 J
|
0 °C
|
735 °C
|
4 hr
|
Ar (I1) EN
|
130 J
|
-20 °C
|
735 °C
|
4 hr
|
Ar (I1) EN
|
60 J
|
-40 °C
|
735 °C
|
4 hr
|
Ar (I1) EN
|
30 J
|
-60 °C
|
焊縫金屬分析
Mn
|
Mo
|
C
|
Si
|
V
|
Ni
|
N
|
Cr
|
0.5 %
|
0.9 %
|
0.1 %
|
0.3 %
|
0.20 %
|
0.5 %
|
8.7 %
|
認(rèn)證:
|
2.0MM, NAKS/HAKC, 07686, VdT?V
|
分類:
|
W CrMo91, EN ISO 21952-A, Wire Electrode, W 62 9C1MV, EN ISO 21952-B, Wire Electrode, ER90S-B9, SFA/AWS A5.28, Wire Electrode
|
認(rèn)證均基于工廠的所在地。如需更多信息,請聯(lián)系伊薩。
合金類型:
|
Alloyed steel (9 % Cr - 1 % Mo - V - N) "9CrMoVN"
|
OK Tigrod 13.38是一種適用于高溫鋼和煉油廠熱氫環(huán)境用鋼GTAW焊接的無鍍銅低合金9CrMoVN焊絲。該焊絲適合用于諸如P 91/T 91鋼等9% Cr鋼種。 該合金的雜質(zhì)元素限值已經(jīng)過修改,因此極其“純凈”。其在室溫和高溫條件下均可獲得較高強度。 AWS已對該產(chǎn)品的歸類進(jìn)行修改。此前歸類編號為A5.9 ER505。
|