Bayblend®
FR410 MT
聚碳酸酯+丙烯腈丁二烯苯乙烯
10%
礦物填料
產品說明:
Rubber modified PC blend; 10 % mineral filled; flame-retardant;
injection molding grade; Vicat/B 120 = 108 °C; very good UL recognition in small
wallthickness (V-0 at 0.75 mm); for railway interiors. Due to the special
formulation of this grade, the final parts may require coating. The
classifications according to the respective rail standards are communicated with
email inquiry under plastics@bayer.com.
|
材料狀態
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區
|
|
|
填料/增強材料
|
|
|
添加劑
|
|
|
特性
|
|
|
RoHS 合規性
|
|
|
加工方法
|
|
|
密度 (23°C)
|
1.30
|
g/cm?
|
ISO
1183
|
|
溶化體積流率（MVR） (260°C/5.0
kg)
|
10.0
|
cm?/10min
|
ISO
1133
|
|
收縮率 3
|
|
|
ISO
294-4
|
|
垂直流動方向 :
260°C, 3.00 mm
|
0.40 到 0.50
|
%
|
|
|
流動方向 :
260°C, 3.00 mm
|
0.40 到 0.50
|
%
|
|
|
吸水率
|
|
|
ISO
62
|
|
飽和,
23°C
|
0.50
|
%
|
|
|
平衡, 23°C,
50% RH
|
0.20
|
%
|
|
|
拉伸模量 (23°C)
|
3950
|
MPa
|
ISO
527-2/1
|
|
拉伸應力
|
|
|
ISO
527-2/50
|
|
屈服,
23°C
|
63.0
|
MPa
|
|
|
斷裂
|
50.0
|
MPa
|
|
|
拉伸應變
|
|
|
ISO
527-2/50
|
|
屈服,
23°C
|
4.0
|
%
|
|
|
斷裂
|
19
|
%
|
|
|
懸壁梁缺口沖擊強度
|
|
|
ISO
180
|
|
-30°C
|
7.0
|
kJ/m?
|
|
|
23°C
|
9.0
|
kJ/m?
|
|
|
熱變形溫度 (1.8 MPa,
未退火)
|
94.0
|
°C
|
ISO
75-2/A
|
|
維卡軟化溫度
|
|
|
|
|
--
|
106
|
°C
|
ISO
306/B50
|
|
--
|
108
|
°C
|
ISO
306/B120
|
|
線形熱膨脹系數
|
|
|
ISO
11359-2
|
|
流動 : 23 到
55°C
|
4.8E-5
|
cm/cm/°C
|
|
|
橫向 : 23 到
55°C
|
5.9E-5
|
cm/cm/°C
|
|
|
UL 阻燃等級
|
|
|
UL
94
|
|
0.750
mm
|
V-0
|
|
|
|
2.00
mm
|
5VB
|
|
|
|
3.00
mm
|
5VA
|
|
|
|
熔體粘度 (260°C, 1000
sec^-1)
|
360
|
Pa·s
|
ISO
11443-A
|
|
在線咨詢 