Lupoy®
GN5001RFD
聚碳酸酯+丙烯腈丁二烯苯乙烯
產品說明:
Description
General Purpose, High
Impact, Halogen Free Flame Retardent
Application
IT/OA(Notebook PC Housing)
|
材料狀態
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區
|
|
|
特性
|
|
|
用途
|
|
|
加工方法
|
|
|
比重
|
1.18
|
g/cm?
|
ASTM
D792
|
|
熔流率（熔體流動速率） (250°C/2.16
kg)
|
18
|
g/10 min
|
ASTM
D1238
|
|
收縮率 - 流動 (3.20 mm)
|
0.40 到 0.60
|
%
|
ASTM
D955
|
|
抗張強度 3 (屈服, 3.20
mm)
|
58.8
|
MPa
|
ASTM
D638
|
|
伸長率 3 (斷裂, 3.20
mm)
|
50
|
%
|
ASTM
D638
|
|
彎曲模量 4 (3.20 mm)
|
2550
|
MPa
|
ASTM
D790
|
|
彎曲強度 4 (屈服, 3.20
mm)
|
93.2
|
MPa
|
ASTM
D790
|
|
懸壁梁缺口沖擊強度 (23°C, 3.20
mm)
|
590
|
J/m
|
ASTM
D256
|
|
載荷下熱變形溫度 (0.45 MPa, 未退火, 6.40
mm)
|
94.0
|
°C
|
ASTM
D648
|
|
RTI Elec
|
|
|
UL
746
|
|
0.850
mm
|
60.0
|
°C
|
|
|
1.00
mm
|
60.0
|
°C
|
|
|
RTI Imp
|
|
|
UL
746
|
|
0.850
mm
|
60.0
|
°C
|
|
|
1.00
mm
|
60.0
|
°C
|
|
|
RTI
|
|
|
UL
746
|
|
0.850
mm
|
60.0
|
°C
|
|
|
1.00
mm
|
60.0
|
°C
|
|
|
UL 阻燃等級
|
|
|
UL
94, IEC 60695-11-10,
-20
|
|
0.850 mm,
ALL
|
V-2
|
|
|
|
1.00 mm,
ALL
|
V-0
|
|
|
|
干燥溫度
|
80.0 到 90.0
|
°C
|
|
|
干燥時間
|
3.0 到 4.0
|
hr
|
|
|
建議的最大水分含量
|
< 0.040
|
%
|
|
|
料筒后部溫度
|
220 到 255
|
°C
|
|
|
料筒中部溫度
|
220 到 275
|
°C
|
|
|
料筒前部溫度
|
245 到 275
|
°C
|
|
|
射嘴溫度
|
245 到 275
|
°C
|
|
|
加工（熔體）溫度
|
245 到 275
|
°C
|
|
|
模具溫度
|
60.0 到 80.0
|
°C
|
|
|
背壓
|
0.981 到 1.96
|
MPa
|
|
|
螺桿轉速
|
40 到 70
|
rpm
|
|