Lupoy®
GP5006AF
聚碳酸酯+丙烯腈丁二烯苯乙烯
產品說明:
Description
Flame Retardant
Application
Elecric and Electronic Housing and
Components
|
材料狀態
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區
|
|
|
特性
|
|
|
用途
|
|
|
UL文件號
|
|
|
加工方法
|
|
|
比重
|
1.17
|
g/cm?
|
ASTM
D792
|
|
熔流率（熔體流動速率） (250°C/2.16
kg)
|
6.0
|
g/10 min
|
ASTM
D1238
|
|
收縮率 - 流動 (3.20 mm)
|
5.0 到 8.0
|
%
|
ASTM
D955
|
|
洛氏硬度 (R 級)
|
108
|
|
ASTM
D785
|
|
抗張強度 3 (屈服, 3.20
mm)
|
51.0
|
MPa
|
ASTM
D638
|
|
伸長率 3 (斷裂, 3.20
mm)
|
60
|
%
|
ASTM
D638
|
|
彎曲模量 4 (3.20 mm)
|
2160
|
MPa
|
ASTM
D790
|
|
彎曲強度 4 (3.20 mm)
|
78.5
|
MPa
|
ASTM
D790
|
|
懸壁梁缺口沖擊強度 (23°C, 3.20
mm)
|
440
|
J/m
|
ASTM
D256
|
|
載荷下熱變形溫度 (1.8 MPa, 未退火, 6.40
mm)
|
104
|
°C
|
ASTM
D648
|
|
RTI Elec
|
|
|
UL
746
|
|
--
|
60.0
|
°C
|
|
|
0.750
mm
|
85.0
|
°C
|
|
|
1.70
mm
|
85.0
|
°C
|
|
|
3.00
mm
|
85.0
|
°C
|
|
|
RTI Imp
|
|
|
UL
746
|
|
--
|
60.0
|
°C
|
|
|
0.750
mm
|
75.0
|
°C
|
|
|
1.70
mm
|
75.0
|
°C
|
|
|
3.00
mm
|
75.0
|
°C
|
|
|
RTI
|
|
|
UL
746
|
|
--
|
60.0
|
°C
|
|
|
0.750
mm
|
75.0
|
°C
|
|
|
1.70
mm
|
75.0
|
°C
|
|
|
3.00
mm
|
75.0
|
°C
|
|
|
體積電阻率
|
1.0E+16
|
ohm·cm
|
ASTM
D257
|
|
介電強度
|
34
|
kV/mm
|
ASTM
D149
|
|
介電常數 (1 MHz)
|
3.00
|
|
ASTM
D150
|
|
耗散因數 (1 MHz)
|
9.0E-3
|
|
ASTM
D150
|
|
耐電弧性 (1.59 mm)
|
100
|
sec
|
ASTM
D495
|
|
耐電弧性 (3.00 mm)
|
PLC 6
|
|
ASTM
D495
|
|
相比耐漏電起痕指數(CTI) (3.00 mm)
|
PLC 2
|
|
UL
746
|
|
高電弧燃燒指數(HAI)
|
|
|
UL
746
|
|
1.70
mm
|
PLC 0
|
|
|
|
3.00
mm
|
PLC 0
|
|
|
|
高壓電弧抗點燃指數 (HVAR)
(PLC) (3.00 mm)
|
PLC 4
|
|
UL
746
|
|
熱絲引燃 (HWI)
|
|
|
UL
746
|
|
1.70
mm
|
PLC 3
|
|
|
|
3.00
mm
|
PLC 2
|
|
|
|
UL 阻燃等級
|
|
|
UL
94
|
|
1.70
mm
|
V-0
|
|
|
|
3.00
mm
|
|
|
|
|
干燥溫度
|
80.0 到 100
|
°C
|
|
|
干燥時間
|
4.0 到 6.0
|
hr
|
|
|
建議的最大水分含量
|
< 0.020
|
%
|
|
|
料筒后部溫度
|
240 到 270
|
°C
|
|
|
料筒中部溫度
|
245 到 275
|
°C
|
|
|
料筒前部溫度
|
245 到 275
|
°C
|
|
|
射嘴溫度
|
245 到 275
|
°C
|
|
|
加工（熔體）溫度
|
240 到 270
|
°C
|
|
|
模具溫度
|
50.0 到 70.0
|
°C
|
|
|
背壓
|
0.981 到 3.92
|
MPa
|
|
|
螺桿轉速
|
40 到 70
|
rpm
|
|